LGHP 2/0.4
High performance, high temperature bearing grease
A premium quality mineral oil based grease, using a modern Polyurea (di-urea) thickener. It is suitable for electric motors and similar applications.
- Extremely long life at high temperatures
- Wide temperature range
- Excellent corrosion protection
- High thermal and mechanical stability
- Good start-up performance at low temperatures
- Compatibility with common polyurea and lithium tickened greases
- Low noise properties
Performance
Speed (max.) n x dm (x 1000) 300 Dropping point (min) ISO 2176 240 °C Base oil viscosity DIN 51562 at 40 °C 96 mm²/s Base oil viscosity DIN 51562 at 100 °C 10.5 mm²/s Penetration DIN ISO 2137, Worked, 60 strokes (10-1mm) 245 – 275 Penetration DIN ISO 2137, Prolonged (max.), 100 000 strokes, 10-1mm 365 max. Mechanical stability – Roll stability, ASTM D1831 (max.) 50 hrs at 80°C, 10-1mm 365 max. Mechanical stability, V2F test, 144 hrs – Corrosion protection, Emcor, ISO 11007, Distilled water 0-0 Corrosion protection, Emcor, ISO 11007 modified, Water washout 0-0 Corrosion protection, Emcor, ISO 11007 modified, 0.5% NaCl 0-0 Water resistance (max.) DIN 51807/1, 3 hrs at 90 °C 1 Oil separation DIN 51817, 40°C, % 3 max. Lubrication ability, R2F test B at 120°C Pass at 100°C Copper corrosion (max.) DIN 51811 /ASTM D4048, 24 hrs at 100°C 1 max. at 150°C Rolling bearing grease life (max.) ROF test, L50 life, 10000 r/min, hrs at °C 1000 at 150°C Low temperature torque, Start/Running, mNm 1000/300 at -40°C Product weight 0.4 kg Properties
DIN 51825 code K2N-40 NLGI consistency class 2-3 Thickener Polyurea Colour Blue Base oil type Mineral Operating temperature range -40 to +150 °C Shelf life 5 year